Halogen free flame retardant MCA is a multifunctional additive with flame retardancy, lubricity and extinction. Its nitrogen content is higher than 48%. In the rubber, plastics, especially in the nylon in a proper amount of additive can play a significant flame retardant; it has good flame retardant effect, small processing smoke, flame retardant grades can reach UL94-V0 level. The product has good thermal stability and long-term heat loss at 300 C, and its heat loss is very low.
At the same time, it has a layered structure similar to graphite and exhibits excellent lubricating properties, and can be used in high temperature, high pressure, high load, impact load conditions; lubrication characteristics of sharp change in high temperature, low temperature, high speed, low speed or temperature conditions is stable. MCA can partly replace molybdenum disulfide and PTFE, and is a kind of material with excellent lubrication effect.
Halogen-free flame retardant MCA products for the smooth white microcrystalline powder, the proportion of 1.5g/cm3, insoluble in water and other organic solvents, but could be better dispersed in oil medium, non-toxic, odorless, tasteless, very stable at 300 degrees Celsius, 600 degrees Celsius above decomposition.
|Appearance：||Creamy white fine powder|
|Total nitrogen (N) content,%:||≥48.00|
|Particle size,%:||25μm： ≥98； 5μm： ≥50|
Chemical name: melamine cyanuric acid, cyanuric acid, melamine salt and so on.
Enterprise standard: Q/JHC001-2016.
CAS number: 37640-57-6.
Halogen free flame retardant MCA can be widely used as flame retardant components in rubber, nylon, phenolic resin, epoxy resin, acrylic emulsion, PTFE resin and other olefin resins. The product can be used as flame retardant insulation materials, high parts, and has excellent lubricating effect of material, can be used as lubricant, grease, lubrication, lubrication performance is better than that of MoS2, but its price is only 1/4.
Flame retardant MCA has non-toxic, no physiological damage, can make the skin compact, smooth, good adhesion to the skin, can be formulated skin cosmetics, can also be used as paint matting agent. In addition, MCA film can be used as antirust lubricating film, steel wire drawing, stamping film stripping agent, as well as the lubrication film of ordinary mechanical transmission parts. Flame retardant MCA can also be made of PTFE, phenolic resin, epoxy resin, polyphenylene sulfide resin and other composite materials, applied to the special requirements of lubricating materials.